An féidir strus a fháil ar steels dhosmálta déphléacsacha?
Féidearthacht faoiseamh struis
D'fhéadfadh strus iarmharach a bheith ag steels dhosmálta déphléacsacha i bhfoirmiú fuar, i meaisínithe nó i dtionól tar éis táthú . De ghnáth, laghdaítear na strusanna seo trí:
Téamh: An miotal a théamh go teocht chuí .
Gabháltas: Sealbhú ag an teocht seo ar feadh tréimhse ama chun strus iarmharach a laghdú .
Fuarú mall: chun forbairt na strusanna iarmharacha breise a íoslaghdú .
Speisialtachtaí steels dhosmálta déphléacsacha
For duplex stainless steels, due to their metallurgical properties, they are prone to the formation of deleterious and unwanted phases at temperatures usually considered for stress relieving. As one handbook states: "No satisfactory temperature below the solution annealing temperature can be used for stress relieving without the danger of forming intermetallic phases that reduce corrosion resistance and reduce diana . "
Faoiseamh struis ar chóimhiotal 2205
I gcás cóimhiotail 2205, is é an teocht tuaslagáin is ísle a luaitear ná 1040 céim {. níos criticiúla, áfach, teastaíonn múchadh tapa ón teocht seo, a thugann cúinsí nua isteach mar dhífhoirmiú agus strusanna iarmharacha breise . Tá cásanna cosúla le haghaidh steels stainle neamhdhíobhálacha eile {}} {}} {}} {}} {}} {}} {}} {}} {} {{{{{}} ag iarraidh go bhfuil siad
Cúinsí praiticiúla
Go praiticiúil, b'fhéidir nach féidir béim a leagan ar tháirgí agus ar threalamh cruach dhosmálta déphléacsacha a mhaolú, ach is féidir teacht ar réitigh ar bhonn cás ar chás, amhail an spreagadh a bhaineann le hoibriú cóireála teasa den sórt sin a bhreithniú sa chéad áit .